Arplas Optimized Process Parameters
Data are Arplas experimentally optimized process parameters -
Mg Bulk Resistivity Comparisons to Al and Steel
Data are bulk resistance measurements (resistivity is calculated from resistance) from ZEK100 and AZ21 compared to Al and steel. -
FSW Process Parameters
Data are experimentally developed process parameters used to produce linear friction stir welded ZEK100 and AZ21 Batch 2 Mg sheet material test coupons for quasi-static lap... -
Electrical Contact Resistance (ECR) Data
Data are electrical contact transition measurements taken in accordance with DIN standard procedure DVS2929-1. -
RSW Electrode Life - AC
Data are RSW A/C welding electrode life evaluations for bare (uncoated) AZ21 Batch 2 (with and without deox) and AZ21 coated with Henkel Process D coating with 75-mm F-type... -
Hot Crack Studies - RSW MFDC
Data are photos of hot cracks resulting from MFDC RSW welding of bare Batch 3 Mg AZ21 with 50-mm F-type electrodes at constant current while varying weld hold times and... -
Bare (uncoated) Mg ZE10A (ZEK100) RSW Evaluation
Data includes process parameter and weld strength results for RSW joining of bare Mg AZ10A. -
RSW Optimized Process Parameters
Data are RSW experimentally optimized process parameters. -
Arplas Weld Quasi-static Strength Evaluation
Data are for quasi-static weld strength measurements for Arplas welded samples. -
Arplas Weld Process Development
Data are weld process parameters related to development of feasible weld process for welding ZEK100, bare AZ21, and AZ21 coated with Henkel Process D. -
RSW MFDC Preliminary Weld Evaluations
Data are measured experimental RSW MFDC weld button sizes and observational comments for welds produced on bare and coated Batch 2 and Batch 3 Mg AZ21 with and without forming... -
Laser Weld Optimized Process Parameters
Data are experimentally optimized laser weld process parameters for AZ21 Batch 3 in bare (uncoated) and coated conditions with and without forming lubes. -
FSW Process Development Images
Data are images of linear FSW weld process development.