Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 300C - 10-3, 10-2 and 10-1 s-1
The UF team seeks to understand the role of Ca and Zn solutes on the texture evolution in Mg. One of the factors related to solte effects on texture is dynamic strain aging... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 250C - 10-3, 10-2 and 10-1 s-1
The UF team seeks to understand the role of Ca and Zn solutes on the texture evolution in Mg alloys. One of the factors related to solute effects on texture is dynamic strain... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 200C - 10-3, 10-2, 10-1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.35Ca (wt.%) 300C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.35Ca (wt.%) 200C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 300C - 10-3, 10-2 and 10-1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 250C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression testing of homogenized Experimental Alloy 1
Compression testing of two homogenized Experimental Alloy 1 samples was performed at room temperature (RT) at 10-3 s-1 on cylindrical samples (10 mm in diameter and 12 mm in... -
Tensile testing of ZK20 and ZEK200 alloys at room temperature - 10-3s-1
Tensile testing of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys at room temperature and strain-rate of 10-3 s-1 -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 200C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca (wt.%) 250C - 10 -1, 10 -2, 10 -3 s-1
Compression stress - strain data of Mg - 0.1Ca (wt.%) compressed at 250C at 10 -3 , 10 -2 , 10 -1 s-1 .