Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 300C - 10-3, 10-2 and 10-1 s-1
The UF team seeks to understand the role of Ca and Zn solutes on the texture evolution in Mg. One of the factors related to solte effects on texture is dynamic strain aging... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 250C - 10-3, 10-2 and 10-1 s-1
The UF team seeks to understand the role of Ca and Zn solutes on the texture evolution in Mg alloys. One of the factors related to solute effects on texture is dynamic strain... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 200C - 10-3, 10-2, 10-1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.35Ca (wt.%) 300C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.35Ca (wt.%) 200C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 250C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression testing of homogenized Experimental Alloy 1
Compression testing of two homogenized Experimental Alloy 1 samples was performed at room temperature (RT) at 10-3 s-1 on cylindrical samples (10 mm in diameter and 12 mm in... -
Compression Mg - 0.35Ca (wt.%) at 250C - 10 - 3, 10 -2 and 10 -1
One of the factors related to solutes effect on texture is dynamic strain aging (DSA) which is observed as serrations in stress - strain curves during compression at high... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 200C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height...