Compression of Mg - 0.1Ca (wt.%) 200C - 10 -1, 10 -2, 10 -3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca, measuring 16 mm in diameter and 24 mm in height... -
Lap Shear Strength Testing EFP Batch 2 PT D
Tested lap shear strength to evaluate possible adhesion weaknesses resulting from applying pretreatment D. -
Corrosion Test Structural Adhesive Over EFP Batch 3 PT D
E-Form Plus lap shear coupons were e-coated (BASF Cathogard 800) and tested in ASTM B117-19 “Salt Fog” (3) environment for 30 days, to evaluate for weakness in corrosion... -
Henkel D v Xtalic Humidity Test
E-form Plus with Henkel pre-treatment “D” was tested side by side with a Zn treatment produced by Xtalic, and electrogalvanized steel panels (ACT), as a control, in a modified... -
Lap Shear Strength Testing EFP Batch 2 PT C
Lap Shear Strength Testing comparing control (as received-Solvent cleaned only) with E-Form plus pretreated with Henkel pretreatment Process C. -
E-Form Plus Batch 2 Surface Analysis
SEM and GDOES of E-Form Plus mg alloy Batch 2, as received.