Compression testing of homogenized Experimental Alloy 1
Compression testing of two homogenized Experimental Alloy 1 samples was performed at room temperature (RT) at 10-3 s-1 on cylindrical samples (10 mm in diameter and 12 mm in... -
Hardness of as-cast and homogenized Experimental Alloy 1
Ten hardness measurements were obtained using a Vickers hardness testing machine with a load of 100 g and a dwell time of 10 s from top, middle and bottom of as-cast and... -
Tensile testing of ZK20 and ZEK200 alloys at room temperature - 10-3s-1
Tensile testing of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys at room temperature and strain-rate of 10-3 s-1 -
Grain size of as-cast and homogenized ZK20 and ZEK200 alloys
Study the effects of RE additions on grain size of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys. -
Compression Mg - 0.35Ca (wt.%) at 250C - 10 - 3, 10 -2 and 10 -1
One of the factors related to solutes effect on texture is dynamic strain aging (DSA) which is observed as serrations in stress - strain curves during compression at high... -
Plane Strain Testing (for FLC0) at Warm Temperatures of Mg eForm Plus Batch-1
Plane Strain Testing (for FLC0) at Warm Temperatures of Mg eForm Plus Batch-1 -
Stability and Cleanability of DOE formulas on E-form PLUS with Henkel pre-tre...
Connected to the Twist Compression Data for the DOE set on E-form PLUS with pre-treatment D; in addition to lubrication testing samples were evaluate for neat product stability... -
Corrosion and Cleanability of Quakerdraw 450 MAG on E-form PLUS with Henkel p...
Results of corrosion, cleanability, and varnishing testing of Quakerdraw 450 MAG (formerly Formula 4C) on E-form PLUS magnesium alloy with Henkel pre-treatment C. -
TCT on E-form PLUS at 250C
Twist Compression Test (TCT) data on E-form PLUS magnesium alloy at 250C. Includes bare E-form PLUS, Henkel pre-treatment C, and Henkel Pre-treatment D -
TCT Data on E-form PLUS at 100C
Twist Compression Test lubrication data performed on E-form PLUS, bare and with Henkel pre-treatment C -
TCT on ZEK100 at 250C
Testing of the lubrication performance by Twist Compression Test (TCT) on ZEK100 at 250C. -
TCT round 1 100C
Lubricant formula screening on ZEK100 Mg Alloy at 100C -
Report 5 - Crossform stamping trial comparing Quaker lubricant with Fuchs Ren...
Blanks were coated with respective lubricants from Quaker Chemicals and Fuchs Lubricants Company. They were stamped into a cross formed (anisotropic) pan. Results were... -
Report 5 - Coefficient of Friction at various temperatures
Summary of the Coefficient of Friction for magnesium at various temperatures with lubricants -
Report 4 - E-Form with Henkel D
Summarizes lab comparisons of the forming properties of Posco E-Form with Henkel "D" pretreatment using lubricants -
Report 3 - EWI Cup Draw results
Summarizes Cup Draw of E Form blanks coated with Renoform 1102 ALWF (lubricant) -
Report 1 - Fuchs Lubricants Co. Initial Lubricant Development and tribology
Summarizes participant's relevant background for the project, approach to lubricant development, and determination of tribology type. -
Initial TGA Screening for Temperature Stability
Thermogravimetric (TGA) analysis of initial formulas screened for thermal stability up to 350C. -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 200C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height...