Compression of Mg - 0.35Ca (wt.%) 200C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 300C - 10-3, 10-2 and 10-1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 250C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca (wt.%) 200C - 10 -1, 10 -2, 10 -3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca, measuring 16 mm in diameter and 24 mm in height... -
X-ray diffraction of as-cast and homogenized Experimental Alloy 1
X-ray diffraction pattern of as-cast and homogenized Experimental Alloy 1. Characteristic peaks of only α-Mg were obtained from (10-1 0), (0002), (10-11), and (10-12) planes. No... -
Grain size of as-cast and homogenized Experimental Alloy 1
Optical micrographs were obtained from the as–cast and homogenized Experimental Alloy 1, from each of the three distinct regions of the ingot labeled top, middle and bottom.... -
Energy dispersive spectroscopy of as-cast and homogenized Experimental Alloy 1
Investigations using SEM revealed the presence of a uniform distribution of AlMn-based (Al8Mn5) intermetallic particles in Mg matrix in both the as-cast and the homogenized... -
Compression testing of homogenized Experimental Alloy 1
Compression testing of two homogenized Experimental Alloy 1 samples was performed at room temperature (RT) at 10-3 s-1 on cylindrical samples (10 mm in diameter and 12 mm in... -
Hardness of as-cast and homogenized Experimental Alloy 1
Ten hardness measurements were obtained using a Vickers hardness testing machine with a load of 100 g and a dwell time of 10 s from top, middle and bottom of as-cast and... -
Tensile testing of ZK20 and ZEK200 alloys at room temperature - 10-3s-1
Tensile testing of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys at room temperature and strain-rate of 10-3 s-1 -
Grain size of as-cast and homogenized ZK20 and ZEK200 alloys
Study the effects of RE additions on grain size of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys. -
Compression Mg - 0.35Ca (wt.%) at 250C - 10 - 3, 10 -2 and 10 -1
One of the factors related to solutes effect on texture is dynamic strain aging (DSA) which is observed as serrations in stress - strain curves during compression at high... -
Plane Strain Testing (for FLC0) at Warm Temperatures of Mg eForm Plus Batch-1
Plane Strain Testing (for FLC0) at Warm Temperatures of Mg eForm Plus Batch-1 -
Simulations of various strain paths with crystal plasticity for Batch_ONE
Crystal plasticity simulations (for Batch_ONE at 200oC) of: - Balanced biaxial tension - Uniaxial compression along RD - Plane strain tension along RD and TD - Simple shear... -
Simulations of various strain paths with crystal plasticity for Batch_THREE
Crystal plasticity simulations (for Batch_THREE at 200oC) of: - Balanced biaxial tension - Uniaxial compression along RD - Plane strain tension along RD - Simple shear along RD... -
FLDs for Batch3 @ 200oC with and without pre-strain
FLD simulations with crystals plasticity -
FLDs for Batch1 @ 150oC, 200oC and 250oC
FLD predictions with crystal plasticity -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 200C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Experiment 1: Tensile Data
Room-temperature tensile data from as-received Mg ZEK100 sheets, tested in rolling direction (RD, 0°), transverse direction (TD, 90°), 30°, 45° and 60°, at 0.0005/s strain rate -
Compression 200C Mg e-Form Batch-3 (M12_UC-200C)
Compression 200C Mg e-Form Batch-3 (M12_UC-200C)