Energy dispersive x-ray spectroscopy of Mg-Ca and Mg-Sn binary alloys for DFT...
To investigate the solid solution strengthening contributions of Ca and Sn, the UIUC team developed physics-based DFT models to simulate unit mechanisms at the dislocation... -
Hardness of Mg-Ca and Mg-Sn binary alloys for DFT solid solution strengthenin...
To investigate the solid solution strengthening contributions of Ca and Sn, the UIUC team developed physics-based DFT models to simulate unit mechanisms at the dislocation... -
Grain size of Mg-Ca and Mg-Sn binary alloys for DFT solid solution strenghten...
To investigate the solid solution strengthening contributions of Ca and Sn, the UIUC team developed physics-based DFT models to simulate unit mechanisms at the dislocation... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 300C - 10-3, 10-2 and 10-1 s-1
The UF team seeks to understand the role of Ca and Zn solutes on the texture evolution in Mg. One of the factors related to solte effects on texture is dynamic strain aging... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 250C - 10-3, 10-2 and 10-1 s-1
The UF team seeks to understand the role of Ca and Zn solutes on the texture evolution in Mg alloys. One of the factors related to solute effects on texture is dynamic strain... -
Compression of Mg - 0.35Ca - 0.5Zn (wt.%) at 200C - 10-3, 10-2, 10-1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.35Ca (wt.%) 300C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.35Ca (wt.%) 200C - 10 -3, 10 -2, 10 -1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.35Ca, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 300C - 10-3, 10-2 and 10-1 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca - 0.5Zn (wt.%) at 250C - 10-1, 10-2, 10-3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca - 0.5Zn, measuring 16 mm in diameter and 24 mm in height... -
Compression of Mg - 0.1Ca (wt.%) 200C - 10 -1, 10 -2, 10 -3 s-1
Compression testing was performed using an Instron 5582 universal testing system on cylindrical samples of Mg – 0.1Ca, measuring 16 mm in diameter and 24 mm in height... -
X-ray diffraction of as-cast and homogenized Experimental Alloy 1
X-ray diffraction pattern of as-cast and homogenized Experimental Alloy 1. Characteristic peaks of only α-Mg were obtained from (10-1 0), (0002), (10-11), and (10-12) planes. No... -
Grain size of as-cast and homogenized Experimental Alloy 1
Optical micrographs were obtained from the as–cast and homogenized Experimental Alloy 1, from each of the three distinct regions of the ingot labeled top, middle and bottom.... -
Energy dispersive spectroscopy of as-cast and homogenized Experimental Alloy 1
Investigations using SEM revealed the presence of a uniform distribution of AlMn-based (Al8Mn5) intermetallic particles in Mg matrix in both the as-cast and the homogenized... -
Compression testing of homogenized Experimental Alloy 1
Compression testing of two homogenized Experimental Alloy 1 samples was performed at room temperature (RT) at 10-3 s-1 on cylindrical samples (10 mm in diameter and 12 mm in... -
Hardness of as-cast and homogenized Experimental Alloy 1
Ten hardness measurements were obtained using a Vickers hardness testing machine with a load of 100 g and a dwell time of 10 s from top, middle and bottom of as-cast and... -
Tensile testing of ZK20 and ZEK200 alloys at room temperature - 10-3s-1
Tensile testing of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys at room temperature and strain-rate of 10-3 s-1 -
Grain size of as-cast and homogenized ZK20 and ZEK200 alloys
Study the effects of RE additions on grain size of as-cast and homogenized ZK20 (Mg-2Zn-0.5Zr wt.%) and ZEK200 (Mg-2Zn-0.5Zr-0.8RE wt.%) alloys. -
Pretreatment of EFP and ZEK-100 Task 3/4 integration
This dataset has no description
-
AZ21 Laser Development and Parameters
This data contains all of the parameters used for laser welding of AZ21 for bare Batch 3 and every lubricant and coating combination. This includes all the parameters used for...